Fabrication and Magnetic Properties of Mn (x) B45Co100-x Alloys

---

Atıf İçin Kopyala

PIYAN C., ŞİMŞEK T., KAYNAR M. B., ÖZCAN Ş.

JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, cilt.29, sa.8, ss.2203-2206, 2016 (SCI-Expanded)

• Yayın Türü: Makale / Tam Makale
• Cilt numarası: 29 Sayı: 8
• Basım Tarihi: 2016
• Doi Numarası: 10.1007/s10948-016-3550-y
• Dergi Adı: JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM
• Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
• Sayfa Sayıları: ss.2203-2206
• Hacettepe Üniversitesi Adresli: Evet

Özet

Mn55-x B45Co (x) bulk alloys with x ranging from 0 to 30 were fabricated by an arc melting technique. Structural properties were investigated by XRD and SEM analysis revealing that Co replaces Mn atoms as x amount increases in the alloy and samples contain two phases with Mn-rich or Co-rich regions. Magnetic properties were characterized by field dependence (M-H) and temperature dependence of magnetization (M-T) measurements using a vibrating sample magnetometer (VSM). Results showed that as x increases from 0 to 30, saturation magnetization decreases from 130 to 53 emu/g. In addition, an increase of the Co content leads a decrease of Curie temperature from 565 to 412 K, enabling the Curie temperature tuning by Co addition.