Amenability of European silver fir (Abies alba Mill.) to preservative treatment by the full-cell process in longitudinal, tangential, radial and triplex flow pathways on the base of wood drying

Usta I.

BUILDING AND ENVIRONMENT, cilt.41, sa.8, ss.1027-1033, 2006 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 41 Sayı: 8
  • Basım Tarihi: 2006
  • Doi Numarası: 10.1016/j.buildenv.2005.04.015
  • Dergi Adı: BUILDING AND ENVIRONMENT
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.1027-1033
  • Hacettepe Üniversitesi Adresli: Evet

Özet

This paper discusses the effects of wood drying upon treatability (as determined by preservative uptake and gain-in-weight retention) of European silver fir on the two moisture content (MC) levels which were designed to be above and below the fibre saturation point (FSP). The treatability behaviour was investigated for individual flow pathways: longitudinal (L, along the stem), tangential (T, along the growth rings) and radial (R, along the rays), and also for the triplex (t, cumulative of all three directions: all faces left open). As the FSP was observed 32.7%, MC of the experimental samples-for each flow path-nominated to around 50% and 9% by recommended kiln drying schedule using a conventional kiln. The samples were then treated with a 2.5% concentration of commercial Tanalith C of CCA (chromium/copper/arsenic) via a mild schedule of full-cell impregnation process using a model pressure treatment plant. Treatability of European silver fir was noticed in different behaviour in either flow paths before and after drying. According to the experimental results, MC regulate the preservative uptake (as the percentage of void volume filled with preservative, VVF%) along the grain (L) and VVF% was improved by kiln drying process effectively, however, it was seemed to be contradictory across the grain (in both T and R). In the cumulative form (1), treatability-in either above or below the FSP - was appeared to be slightly greater than that for L due to support of the longitudinal flow. Therefore.. it could be suggested that wood material which is subjected to be used in constructional purposes has to be initially dried to below the FSP, and-for efficient preservative treatment - it has to be treated with all faces unsealed (free from any pre-coating and/or painting). This shall be more ideal which in turn influences the quality of treated wood allowing better performance in its service life. (C) 2005 Elsevier Ltd. All rights reserved.