Preparation, characterization and electrical behaviors of greenish single-chain polymeric molecule-via intramolecular ball type cobalt phthalocyanines/ graphite oxide composites


DEMİRELLİ K., Abubakar A. M., TUNCER H., SALİH B.

JOURNAL OF MOLECULAR STRUCTURE, cilt.1235, 2021 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 1235
  • Basım Tarihi: 2021
  • Doi Numarası: 10.1016/j.molstruc.2021.130132
  • Dergi Adı: JOURNAL OF MOLECULAR STRUCTURE
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Chemical Abstracts Core, INSPEC
  • Hacettepe Üniversitesi Adresli: Evet

Özet

The greenish single-chain polymeric molecule-ball type CoPc (SCPM-ball type CoPc) was prepared via the intramolecular formation of cobalt phthalocyanine from polystyrene-co-poly[4,4 '-((((4-vinylbenzyl)azanediyl)bis(ethane-2,1diyl))bis(oxy))diphthalonitrile] [P(PNDEAMSt12%-co-St)] (linear copolymer precursor) under diluted conditions at 150 degrees C. The structure of SCPM-ball type CoPc was confirmed by FT-IR, MALDI-TOF-MS, UV and SEM. The conversion dependence of the experimental activation energy was readily determined by an isoconversional method. So, the Flynn-Wall-Ozawa (FWO) and Kissinger-Akahira-Sunose (KAS) showed that the linear copolymer precursor's activation energies were as average 128.7 kJ/mol and 124.0 kJ/mol and those of SCPM-ball type CoPc were average 161.9 kJ/mol and 153.8 kJ/mol, respectively. Conductivity mechanism of composites was suggested as Correlated Barrier Hoping (CBH). The linear copolymer precursor/graphite oxide (GO) composite has a significant performance for dielectric constant of 696.4 at 130 degrees C, but it was with a comparatively greater dielectric loss. Those of SCPM-ball type CoPc/14wt% GO increased virtually the same relative ratio. (c) 2021 Elsevier B.V. All rights reserved.